X12CrMnNiN18-9-5 (1.4373) Austenitic
| Name Designation EN | X12CrMnNiN18-9-5 |
| Number | 1.4373 |
| AISI ASTM | 202 |
| Grades | Austenitic |
| Chemical Composition (Cast Analysis) | |||||||||
| C | Si | Mn | Pmax | S | N | Cr | Mo | Ni | Others |
| ≤0.15 | ≤1.00 | 7.50 to 10.5 | 0.045 | ≤0.015 | 0.05 to 0.25 | 17.00 to 19.00 | 4.00 to 6.00 | ||
| Mechanical Properties | |||||||||
| Thickness (Max) | Heat Treatment | Hardness (Max) | Proof Strength | Tensile Strength | Elongation after fracture | Impact Energy | |||
| [mm] | HRB | HB or HV | Rp 0.2 [MPa) |
Rm [MPa] |
A80mm [%] min |
A [%] min |
KV [J] min |
||
| transverse | th < 3mm (tri & long) |
th ≥ 3mm (tr. & long.) |
long. | transv. | |||||
| 8 | AT | 90 | 241 | 350 | 680 – 880 | 45 | 45 | ||
| 13.5 | 320 | 100 | 60 | ||||||
| 75 | 320 | 35 | 35 | ||||||
| Physical Properties | ||||||
| Density @ 20degC | Modulus of Elasticity 20⁰C |
Mean Coefficient of Thermal Expansion 10^-6 xK^-1 |
Thermal Conductivity @ 20⁰C |
Specific Heat @ 20⁰C |
Electrical Resistivity @ 20⁰C |
|
| [kg/dm^3 | [GPa] | 20⁰C – 200⁰C | 20⁰C – 400⁰C | [W/(mxK)] | [J/(kgxK)] | [Ωxmm^2/m] |
| 7.8 | 200 | 17.5 | 18.4 | 15 | 503 | 0.7 |